High Carbon Steel Shot SAE S110 for Surface Cleaning and Metal Surface Treatment
High carbon steel shot
High carbon steel shot is used in the majority of the wheel blast applications and creates a dimpled, peened surface. Only the shot's skin suffers from
the impact and very thin flakes will progressively part from the shot, which itself stays round throughout its life cycle. Our steel shot is very durable
with high resistance to impact fatigue, giving it an effective and quick cleaning rate.
Application
·Sand removal of large sized castings, scale removal of large sized products from forging,stamping, dieforging, drawing and rolling or after heat treatment (e.g. pipes, sections, plates,fittings, wire).
·Sand removal of large and medium sized castings, scale removal of forging and heat-treated work pieces, surface blast cleaning of steel plates, sections and steel structures, shot peening of work pieces, cutting of granite.
·Sand removal of medium and small sized castings, surface blast cleaning of forgings, heat-treated pieces,steel pipes, sections and steel structures, surface treatment before painting,shot peening of work pieces.
|
SPECIFICATION HIGH CARBON STEEL SHOT
|
| Chemical composition |
(C):0.80-1.20% |
(Mn): 0.35-1.20% |
(Si):≥0.40% |
(S):≤0.05% |
(P): ≤ 0.05% |
| Hardness |
40 - 50HRC, 52 - 57HRC |
| Hardness Deviation |
Max. deviation ±3.0 HRC |
| Microstructure |
Tempered martensite or tempered troostite |
| Density |
>7.2 g/cm³ |
| Bulk density |
4.4 g/cm³ |
|
Mesh
|
mm |
SS-2.5 |
SS-2.0 |
SS-1.7 |
SS-1.4 |
SS-1.2 |
SS-1.0 |
SS-0.8 |
SS-0.6 |
SS-0.5 |
SS-0.3 |
SS-0.2 |
|
7
|
2.80 |
ALL PASS |
|
|
|
|
|
|
|
|
|
|
|
8
|
2.36 |
|
ALL PASS |
|
|
|
|
|
|
|
|
|
|
10
|
2.00 |
85% MIN |
|
ALL PASS |
ALL PASS |
|
|
|
|
|
|
|
|
12
|
1.70 |
97% MIN |
85% MIN |
|
5% MAX |
ALL PASS |
|
|
|
|
|
|
|
14
|
1.40 |
|
97% MIN |
85% MIN |
|
5% MAX |
ALL PASS |
|
|
|
|
|
|
16
|
1.18 |
|
|
97% MIN |
85% MIN |
|
5% MAX |
ALL PASS |
|
|
|
|
|
18
|
1.00 |
|
|
|
96% MIN |
85% MIN |
|
5% MAX |
ALL PASS |
|
|
|
|
20
|
0.85 |
|
|
|
|
96% MIN |
85% MIN |
|
10% MAX |
ALL PASS |
|
|
|
25
|
0.71 |
|
|
|
|
|
96% MIN |
85% MIN |
|
10% MAX |
|
|
|
30
|
0.60 |
|
|
|
|
|
|
96% MIN |
85% MIN |
|
ALL PASS |
|
|
35
|
0.50 |
|
|
|
|
|
|
|
97% MIN |
85% MIN |
10% MAX |
|
|
40
|
0.425 |
|
|
|
|
|
|
|
|
96% MIN |
|
ALL PASS |
|
45
|
0.355 |
|
|
|
|
|
|
|
|
|
80% MIN |
10% MAX |
|
50
|
0.30 |
|
|
|
|
|
|
|
|
|
90% MIN |
|
|
80
|
0.18 |
|
|
|
|
|
|
|
|
|
|
80% MIN |
|
120
|
0.12 |
|
|
|
|
|
|
|
|
|
|
90% MIN |
|
200
|
0.075 |
|
|
|
|
|
|
|
|
|
|
|
|
325
|
0.045 |
|
|
|
|
|
|
|
|
|
|
|
| SAE J444 |
S-780 |
S-660 |
S-550 |
S-460 |
S-390 |
S-330 |
S-280 |
S-230 |
S-170 |
S-110 |
S-70 |